- TPEG
- Monomer for PCE Production
- Polyether monomer
Quick Details
- ProName: Polyether monomer (Raw material of pol...
- CasNo: 62601-60-9
- Molecular Formula: CH2=CH(CH3)CH2CH2O(CH2CH2O)nH
- Appearance: white flake
- Application: TPEG is a new complex raw material of ...
- DeliveryTime: 7-14working days
- PackAge: 25kg/bag
- Port: Guangzhou,China
- ProductionCapacity: 700 Metric Ton/Month
- Purity: 100%
- Transportation: FOB,CFR,CIF
- LimitNum: 0 Metric Ton
- Grade: Industrial Grade
- Hydroxyl value(MgKOH/g): 20-25
- PH value(1% water solution): 5-7
- Degree of unsaturation(mol/kg): 0.39min
Superiority
- High active catalyst and special synthesis technical process
- Soluble in water and other solvents
- Excellent adaptability to cement
- Water reducing rate can be up to 30% if adding 1.1%TPEG into concrete.
- Improving early strength and strength after 28days. Compressive strength 1day:180Min,3days:170Min,7days:160Min,28days:150Min
- Greatly reduce W/B ratio,shrinkage and creep,improving durability.
- Low slump loss,slump retention index:190Min
- The water reducer made by TPEG has a good appearance and quality.
Details
Polyether monomer (Raw material of polycarboxylate superplasticizer)
Chemical structure:CH2=CH(CH3)CH2CH2O(CH2CH2O)nH
CAS No.: 62601-60-9
Product introduction
TPEG is a new complex raw material of high performance polycarboxylate water reducer researched&developed by our company.High performance polycarboxylate water reducer has passed testing and checking by authorized organization and fully conform with polycarboxylate water reducer standard and requirement for temporary technical conditions of high performance concrete passenger transportation special line.
Application
TPEG is mainly for manufacturing high performance polycarboxylate water reducer.
Technical specification
Item |
Index |
Appearance |
White flake |
Hydroxyl value(MgKOH/g) |
20~25 |
PH value(1% water solution) |
5~7 |
Degree of unsaturation(mol/kg) |
0.39 Min |
Double bond retention(%) |
90 Min |
Product characteristic
- High active catalyst and special synthesis technical process
- Soluble in water and other solvents
- Excellent adaptability to cement
- Water reducing rate can be up to 30% if adding 1.1%TPEG into concrete.
- Improving early strength and strength after 28days. Compressive strength 1day:180Min,3days:170Min,7days:160Min,28days:150Min
- Greatly reduce W/B ratio,shrinkage and creep,improving durability.
- Low slump loss,slump retention index:190Min
- The water reducer made by TPEG has a good appearance and quality.
Package and storage
Package:25kg/bag
TPEG is non-hazardous,it is intoxic and hard to burn.
Self-life is normally 6months and stored at cool and ventilated place.